At low Cr contents, no internal oxidation zone is seen. This is because the rateat which the external scale is formed is so rapid that the thickness of the internaloxidation zone is negligibly small. On increasing the Cr content, Fe2+ ions are progressively blocked by the FeCr2O4islands and the FeO layer correspondingly becomes thinner relative to the Fe3O4-layer thickness