Abstract: The super-hydrophobic cop

Abstract: The super-hydrophobic copper surface was obtained by using a nanosecond pulsed laser.Different micro- and nano-structures were fabricated by changing the laser scanning interval andscanning speed, before heating in an electric heater at 150 ◦C for two hours to explore the effect of laser parameters and heat treatment on the wettability of the copper surface. It was found that the laser-treated copper surface is super-hydrophilic, and then, after the heat treatment, the surface switches to hydrophobic or even super-hydrophobic. The best super-hydrophobic surface’s apparent contact angle (APCA) was 155.6◦ , and the water sliding angle (WSA) was 4◦. Super-hydrophobic copper is corrosion-resistant, self-cleaning, and dust-proof, and can be widely used in various mechanical devices.

結果 (繁體中文) 1:

摘要：
通過使用納秒脈衝激光所得到的超疏水性的銅表面。
不同微米和納米結構通過改變激光掃描間隔和製造
的掃描速度，在150◦C中的電加熱器加熱兩小時以探索的激光參數和熱處理對銅表面的潤濕性的效果之前。
已經發現，激光處理的銅表面是超親水性的，然後，在熱處理後，在表面切換到疏水性或甚至超疏水。最好超疏水表面的表觀接觸角（APCA）為155.6◦，水滑角（WSA）是4◦。
超疏水銅是耐腐蝕，自清潔，和防塵，並能廣泛用於各種機械裝置。

結果 (繁體中文) 2:

ระบบการผลิตแบบลีนขั้นพื้นฐานสำหรับการเป็นผู้ช่วยผู้ฝึกสอน

結果 (繁體中文) 3:

摘要：
利用納秒脈衝雷射獲得了超疏水銅表面。
通過改變雷射掃描間隔，製備了不同的微納米結構
掃描速度，在150°C電加熱器中加熱兩小時前，探討雷射參數和熱處理對銅表面潤濕性的影響。
結果表明，雷射處理後的銅表面具有超親水性，熱處理後的銅表面轉變為疏水性甚至超疏水性。最佳超疏水表面的錶觀接觸角（APCA）為155.6°；滑水角（WSA）為4°。
超疏水銅具有耐腐蝕、自清潔、防塵等優點，可廣泛應用於各種機械設備中。