High-boron high-speed steel roll ma

High-boron high-speed steel roll materials used
50 kg alkaline medium-frequency induction furnace
melting. High-speed steel scrap, steel scrap, pig iron,
ferromolybdenum, ferrotungsten, ferrovanadium,
ferrochrome and ferroboron were used to make-up
of charge. Ferrochrome is added after the molten
steel melt is cleared, and ferrovanadium and
ferroboron are added before tapping. Liquid steel
tapping temperature is 1530
–
1560 °C. Pouring tem-
perature is 1460
–
1480 °C. With sand casting shap-
ing, casting into 20 mm × 20 mm × 120 mm speci-
men. Then using wire cutting machine directly take
into 20 mm × 20 mm × 20 mm specimens and
10 mm × 10 mm × 55 mm specimens, and conduct-
ed microstructure observation and mechanical prop-
erties test, respectively. Specific compositions of the
specimen are shown in Table 1.

結果 (中文) 1:

高硼高速钢轧辊材料50 公斤碱性中频感应电炉融化。高速的废钢、 废钢、 生铁、钼铁、 钨铁、 钒铁，铬铁、 硼铁被用来化妆电荷。铬铁被添加后熔清除了钢液，和钒铁和攻丝前添加硼铁。钢液攻丝温度是 1530–1560 ° C。倾吐透射电镜-温度是 1460–1480 ° C。与砂型铸造十八-ing，铸造成 20 毫米 × 20 毫米 × 120 毫米规格-男子。然后直接使用线切割机床到 20 毫米 × 20 毫米 × 20 毫米标本和10 毫米 × 10 毫米 × 55 毫米标本和行为.教育署微观结构观察及机械道具-特性的测试，分别。具体成分标本如表 1 所示。

結果 (中文) 3:

高硼高速钢轧辊材料50公斤碱性中频感应炉熔化。高速钢废钢，废钢、生铁，钨铁、钼铁、钒铁，铬铁、硼铁合金用于化妆电荷。铬铁是后添加液钢液被清除，钒铁和硼铁加入攻丝前。钢液出钢温度是1530–1560°C.浇注—温度是1460–1480°C.与砂型铸造形状—ING，浇铸成20毫米20毫米120毫米规格××—男人。然后用线切割机直接拿为20毫米20毫米20毫米××标本10毫米10毫米55毫米××标本，并进行—ED显微组织观察和力学性能—性能测试，分别。的具体成分标本如表1所示。