The standard specimen for ASTM is 6

The standard specimen for ASTM is 64 x 12.7 x 3.2 mm (2½ x ½ x 1/8 inch). The most common specimen thickness is 3.2 mm (0.125 inch), but the preferred thickness is 6.4 mm (0.25 inch) because it is not as likely to bend or crush. The depth under the notch of the specimen is 10.2 mm (0.4 inches). The standard specimen for ISO is a Type 1A multipurpose specimen with the end tabs cut off. The resulting test sample measures 80 x 10 x 4 mm. The depth under the notch of the specimen is 8mm.ASTM impact energy is expressed in J/m or ft-lb/in. Impact strength is calculated by dividing impact energy in J (or ft-lb) by the thickness of the specimen. The test result is typically the average of 5 specimens. ISO impact strength is expressed in kJ/m2. Impact strength is calculated by dividing impact energy in J by the area under the notch. The test result is typically the average of 10 specimens.Netherlands

結果 (繁體中文) 1:

為ASTM標準樣品是64×12.7×3.2毫米（2.5 X 8.5×1/8英寸）。最常見的試樣厚度為3.2mm（0.125英寸），但優選的厚度為6.4毫米（0.25英寸），因為它是不作為可能彎曲或破碎。試樣的缺口下的深度為10.2毫米（0.4英寸）。

對於ISO標準樣品是1A型多用途與切斷端片樣品。將得到的試驗樣品測量80×10×4毫米。試樣缺口下的深度為8mm。
ASTM衝擊能量以J /米或英尺-磅/英寸表示。衝擊強度通過由試樣的厚度除以衝擊能量以J（或英尺-磅）來計算。試驗結果通常是平均5個試樣的。

ISO衝擊強度是千焦/平方米表示。衝擊強度是由缺口下的面積除以衝擊能量以J計算。該試驗結果通常是平均10個樣品。
荷蘭

結果 (繁體中文) 2:

ASTM 的標準試樣為 64 x 12.7 x 3.2 毫米（21⁄2 x 1/2 x 1/8 英寸）。最常見的試樣厚度為 3.2 毫米（0.125 英寸），但首選厚度為 6.4 毫米（0.25 英寸），因為它不太可能彎曲或壓碎。試樣槽口下的深度為 10.2 毫米（0.4 英寸）。

ISO 的標準試樣是 1A 型多用途試樣，端片被切斷。生成的測試樣本尺寸為 80 x 10 x 4 mm。試樣槽口下的深度為8mm。
ASTM 衝擊能量以 J/m 或 ft-lb/表示。衝擊強度的計算方法是將衝擊能量除以 J（或 ft-lb）除以試樣厚度。測試結果通常是 5 個試樣的平均量。

ISO 衝擊強度以 kJ/m2 表示。衝擊強度的計算方法是將 J 中的衝擊能量除以陷波下方的區域。測試結果通常是平均 10 個樣本。
荷蘭

結果 (繁體中文) 3:

ASTM標準試樣為64 x 12.7 x 3.2 mm（2/2 x 1/8英寸）。最常見的試樣厚度為3.2 mm（0.125英寸），但首選厚度為6.4 mm（0.25英寸），因為它不太可能彎曲或壓碎。試樣缺口下的深度為10.2 mm（0.4英寸）。
ISO的標準試樣為1A型多用途試樣，端部凸耳被切斷。得到的試樣尺寸為80 x 10 x 4 mm。試樣缺口下的深度為8mm。
ASTM衝擊能用J/m或ft-lb/in表示。衝擊強度是通過將衝擊能量（組織：J（或ft-lb））除以試樣厚度來計算的。測試結果通常是5個樣本的平均值。
ISO衝擊強度用kJ/m2表示。衝擊強度的計算方法是將衝擊能量（J）除以缺口下的面積。試驗結果通常為10個試樣的平均值。
荷蘭