遭受火害700℃時，純水泥混凝土與水淬高爐石混凝土，其殘留應力控制因素

遭受火害700℃時，純水泥混凝土與水淬高爐石混凝土，其殘留應力控制因素皆為試體的含水量，單位體積內的含水量越少，強度折減越少。