a)shows the sintered densities of Al2O3-10vol.% ZrO2 specimens from hydrolysis fired at 1600 °C for 3 hrs.When the pH after hydrolysis was low, primary particle size was small but due to the difficulty of removal Cl ion, the specimen was poorly sinterable.